FABRICS

Marglass ALL450

Composition: 98% E-Glass + 2% Aluminum (1050 Alloy)
Coating: 12μm Aluminum Foil (One Side)
Weave: Satin
Weight: 450 g/m²
Thickness: 0.4mm
Continuous Use Temperature: 450°C
Instant Temperature Resistance: 550°C
Radiant Heat Reflectance: 750°C-850°C
Limited Flame Spread: ISO 15025: A1-A2
Convective Heat:ISO 9151: B1
Radiant Heat:ISO 6942: C4
Mechanical Strength:ISO 4606: 2400N - 2000N
Waterproof:EN 20811: 170,000 Pa

Marglass ALP450NT

Composition: 48% E-Glass + 44% Preox + 8% Aluminum
Coating: 12μm Aluminum Foil (One Side)
Weight: 450 g/m²
Thickness: 2.6mm
Continuous Use Temperature: 650°C
Instant Temperature Resistance: 1300°C
Limited Flame Spread: ISO 15025: A1
Convective Heat: ISO 9151: B2
Radiant Heat:ISO 6942: C4
Contact Temperature:ISO 12127: F2
Mechanical Strength:ISO 4606: 2200N - 1200N

Marglass PTFE100

Composition: 58% PTFE + 42% E-Glass

Coating: 70 g/m² PTFE (Double Face)

Weave: Plain

Weight: 250 g/m²

Thickness: 0.12mm

Continuous Use Temperature: -150°C / 260°C

Instant Temperature Resistance: 260°C

Limited Flame Spread ISO 15025: A1-A2

Mechanical Strength EN 13934-1: 1450N - 1300N

Tear Strength EN 13537/2: 20N - 18N

Moisture Absorption: 0.005%

Marglass PU650IN

Composition: 75% E-Glass + 15% Polyurethane + 10% Stainless steel
Coating: 100 g/m² Polyurethane Coating (Double Sides)
Weave: Plain
Weight: 650 g/m²
Thickness: 0.6mm
Continuous Use Temperature: 550°C
Instant Temperature Resistance: 750°C
Limited Flame Spread: ISO 15025: A1-A2
Mechanical Strength : ISO 4606: 1500N - 3000N
Abrasion Resistance : (8hrs/650°C) - ISO 12947-2: > 8,000 Cycles

Composition: 84% E-Glass + 16% HT Silicone
Coating: 80 gr/m² HT Silicone Coating (Single Side)
Weave: Satin
Weight: 490 g/m²
Thickness: 0.4mm
Continuous Use Temperature: 250°C
Instant Temperature Resistance: 550°C
Limited Flame Spread ISO 15025: A1-A2
Convective Heat ISO 9151: B1
Radiant Heat ISO 6942: C1
Mechanical Strength ISO 4606: 2700N - 1700N
Waterproof: EN 20811: 100 Pa
Flame Resistance Level UNE 23727: M0

Composition: 72% E-Glass + 28% HT Silicone
Coating: 80 gr/m² HT Silicone Coating (Double Side)
Weave: Satin
Weight: 590 g/m²
Thickness: 0.5mm
Continuous Use Temperature: 300°C
Instant Temperature Resistance: 900°C
Limited Flame Spread: ISO 15025: A1-A2
Convective Heat: ISO 9151: B1
Radiant Heat: ISO 6942: C1
Mechanical Strength : ISO 4606: 2700N - 1700N
Waterproof : EN 20811: 100 Pa
Flame Resistance Level : UNE 23727: M0

Composition : 62% E-Glass + 28% Preox + 10% HT Silicone
Coating : 80 gr/m² HT Silicone Coating (Single Side)
Coating : Nonwoven Preox (One Side)
Weave : Satin
Weight : 730 g/m²
Thickness : 2.1mm
Continuous Use Temperature: 550°C
Instant Temperature Resistance: 1300°C
Limited Flame Spread: ISO 15025: A1-A2
Melt Drip : ISO 9150/EN 11611: Class 2
Convective Heat : ISO 9151: B1
Radiant Heat : ISO 6942: C1
Mechanical Strength : ISO 4606: 2700N - 1700N
Waterproof : EN 20811: 100 Pa
Melted Metal Splash : EN ISO 9185: D3/E3
Abrasion Resistance: ISO 12947-2: > 20,000 Rounds

Composition : Silicate
Coating : Vermiculite (Double Face)
Weave : Satin
Weight : 650 g/m²
Thickness : 0.7mm
Continuous Use Temperature: 950°C
Instant Temperature Resistance: 1300°C
Flame Resistance Level : UNE 23.102-90: M-0
Convective Heat : ISO 9151: B1
Mechanical Strength : ISO 4606: 15kg/cm - 30kg/cm

Marglass OX730IN

Composition : 80% E-Glass + 18% Metal Oxide + 2% Stainless steel
Coating : 65 gr/m² Metal Oxide (Double Face)
Weight : 730 g/m²
Thickness : 0.9mm
Continuous Use Temperature: 700°C
Instant Temperature Resistance: 750°C
Limited Flame Spread: ISO 15025: A1-A2
Mechanical Strength : EN 13934-14: 3000N - 1500N
Abrasion Resistance: (8s/650°C) - ISO 12947-2: >8000

Composition : 72% E-Glass + 28% Vermiculite
Coating : Vermiculite (Double Face)
Weave : Plain
Weight : 1035 g/m²
Thickness : 1.3 mm
Continuous Use Temperature : 800°C
Instant Temperature Resistance: 1000°C
Limited Flame Spread: ISO 15025: A1-A2
Mechanical Strength : ISO 4606: 4500N - 2500N